Preparation and properties of long afterglow in alkaline earth silicate phosphors co-doped by Eu2O3 and Dy2O3

Sr2MgSi2O7 host doped with Eu, Dy ions with high brightness and long afterglow was prepared by sintering at high temperature under weak reductive atmosphere. The luminescent properties of this photoluminescent pigment have been systematically studied. The analytical results indicated that the co-doped Eu and Dy ions have little influence on the structure of luminescent materials. That main emission peaks appeared at 469 nm and belonging to a broad-emission is ascribed to the 4f7→4f65d1 transition of Eu2+ in the pigment matrix. The pigment doped only with Eu ions did not have the long afterglow phenomenon. But while co-doped Dy3+ ions in the pigment matrix, the obvious long afterglow was observed, and its decay process contained fast-decay and slow-decay processes