Synthesis of amorphous alloys and amorphous-crystalline composites in the Cu-Nb-Hf system by ion beam mixing

Seven sets of Cu-Nb-Hf multilayered films were designed and prepared with the overall compositions of Cu21Nb65Hf14, Cu33Nb49Hf18, Cu34Nb34Hf32, Cu34Nb10Hf56, Cu50Nb23Hf27, Cu58Nb10Hf32, and Cu70Nb8Hf22, and an ion beam mixing experiment was then conducted using 200 keV xenon ions. It is found that the Cu-Nb-Hf system is a metallic glass forming one, and the single amorphous alloys could be synthesized in the Cu-Nb-based alloys with less than 18 at.% of Hf as a third addition. Also, when the Hf concentration is greater than 18 at.%, i.e., at the compositions of Cu34Nb34Hf32, Cu34Nb10Hf56, Cu50Nb23Hf27, Cu58Nb10Hf32, and Cu70Nb8Hf22, ion beam mixing resulted in the formation of amorphous-crystalline composites, which might have better mechanical properties than single-phase glassy alloys. In addition, a detailed discussion was presented for the formation mechanism of the amorphous alloys and amorphous-crystalline composites.