Thermal and electrical properties of Ca₅Mg_4−xZn_x(VO₄)₆ (0 ≤ x ≤ 4)

Calcium vanadates Ca₅Mg_4−xZn_x(VO₄)₆ (0 ≤ x ≤ 4) have been studied for the first time using a set of high-temperature methods of analysis. The onset of melting process determined from differential scanning calorimetry decreases from 1158 to 881 °C (± 1.5 °C) with increasing of x (dopant's content). CTE temperature dependence is found to show a hysteresis. Electrical transport properties measured by impedance spectroscopy in air of different humidity are also discussed. The value of electrical conductivity does not depend on air humidity. It is found to equal to 1.5 × 10⁻⁶ S cm⁻¹ at 720 °C for Ca₅Mg₄(VO₄)₆ which is specific for garnet-related crystals.