Influence of Ca substitution by Mg on the Ca3Co4O9 performances

Ca3-xMgxCo4O9 polycrystalline thermoelectric ceramics with small amounts of Mg have been synthesized by the classical solid state method. Microstructural characterizations have shown that all the Mg has been incorporated into the Ca3Co4O9 structure and no Mg-based secondary phases have been identified. Apparent density measurements have shown that samples do not modify their density until 0.05 Mg content, decreasing for higher contents. Electrical resistivity decreases and Seebeck coefficient slightly raises when Mg content increases until 0.05 Mg addition. The improvement in both parameters leads to higher power factor values than the usually obtained in samples prepared by the conventional solid state routes and close to those obtained in textured materials. (Author)