Electronic transfer through Langmuir-Blodgett layers of capped platinum nanoparticles: An electrochemical approach

Amine functionalized platinum nanoparticles have been modified by over-grafting two different molecules, 2-thiophenecarbonyl chloride (Pt-1) and 1-hexyl-4-(4-isothiocyanatophenyl)-bicyclo (2, 2, 2) octane (Pt-2). Cyclic voltammetry was performed at gold electrodes coated with Langmuir-Blodgett (LB) mixed films of Pt-1 and Pt-2 nanoparticles, and behenic acid. From five layers the electrochemical response was essentially provided by the last LB component. The electrochemical responses towards the [Fe(CN)6]3-/4- couple were strongly influenced by the nature of the over-grafted molecules: films of Pt-2 presented an almost complete blocking effect, while films of Pt-1 allowed the redox reaction to occur on Pt nanoparticles. In order to understand the reasons for such different behaviors we built up hetero-nanostructures by superposing Pt-1 and Pt-2 LB layers in different ways, yielding different kinds of 'sandwich' structures. The electrochemical response depended on the electrode ending. When Pt-1 nanoparticles were in the outer layer, in contact with the electrolyte solution, the electrode was electroactive toward the redox probe, while when Pt-2 layers were in the outer layer no electroactivity was detected. For sandwiches made of Pt-1, with a variable thickness of an intercalated film of Pt-2, the electrode response to [Fe(CN)6]3-/4- was modulated by the thickness of the inter-layer: the thicker the layer, the lower the response