CVD synthesis of carbon nanotubes using a finely dispersed cobalt catalyst and their use in double layer electrochemical capacitors

Carbon nanotubes (CNT) were obtained by chemical vapour deposition (CVD), decomposing turpentine oil over finely dispersed Co metal as a catalyst at 675 deg. C. Scanning electron microscope (SEM) and transmission electron microscope (TEM) images reveal that the nanotubes are densely packed and of 10-50 nm in diameter. The XRD pattern of purified CNT shows that they are graphitic in nature. Resistivity measurements of these CNT indicate that they are highly conducting. Hall measurements of CNT reveal that electrons are the majority carriers with a carrier concentration of 1.35x1020 cm-3. Cyclic voltammetry (CV) and constant current charging/discharging was used to characterise the behaviour of electrochemical double layer capacitors of purified CNT with H2SO4. For CNT/2 M H2SO4/CNT, a capacitance of 12 F g-1 (based on the weight of the active material) was obtained