Conductivity, magnetoresistance and specific heat of oxygen-deficient La0.67Sr0.33MnO3-α (0 ≤ α ≤ 0.16)
- 1. RAN, Fiziko-Tekhnicheskij Inst. im. A.F. Ioffe, Sankt-Peterburg (Russian Federation)
Description
The results of studying the La0.67Sr0.33MnO3-α oxygen-deficient solid solutions are presented. Comparison with the results of studying the similar series of the lanthanum-calcium manganites is carried out. The physical characteristics of both series are explained on the basis of the change in the Mn3+/Mn4+ ratio by the oxygen recovery. The differences between the strontium and calcium series are conditioned by the differences in the volumetric properties of the source full-set oxygen-containing materials and the materials texture. The latter one is manifested in the effect of the intergranular magnetoresistance, exceeding by the absolute value the effect of the colossal magnetoresistance, conditioned by the internal properties of the material. The peculiarities of the electrophysical parameters dependence on the temperature and Mn4+ ratio are determined for the oxygen-deficient La0.67Sr0.33MnO3-α
Abstract (Russian)
Представлены результаты исследования кислород-дефицитных твердых растворов La0.67Sr0.33MnO3-α. Проведено сравнение с результатами исследования такой же серии лантан-кальциевых манганитов. Физические характеристики обеих серий объясняются на основе изменения соотношения Mn3+/Mn4+ при извлечении кислорода. Различия стронцевой и кальциевой серий обусловлены различиями как объемных свойств исходных полнокомплектных по кислороду материалов, так и текстуры материалов. Последняя проявляется у стронциевой серии в эффекте межгранульного магнетосопротивления, превышающего по абсолютной величине эффект колоссального магнетосопротивления, обусловленный внутренними свойствами материала. Для кислород-дефицитного La0.67Sr0.33MnO3-α выявлены особенности зависимости электрофизических параметров от температуры и доли Mn4+. Обсуждается физический смысл этих различий. Предложена модифицированная диаграмма состояния: температуры фазовых переходов - доля Mn4+Additional details
Additional titles
- Original title (Russian)
- Проводимость, магнетосопротивление и теплоемкость кислород-дефицитного La...
Publishing Information
- Journal Title
- Fizika Tverdogo Tela
- Journal Volume
- 46
- Journal Issue
- 11
- Journal Page Range
- p. 2018-2024
- ISSN
- 0367-3294
- CODEN
- FTVTAC
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 37019976
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- LANTHANUM OXIDES; MAGNETORESISTANCE; MANGANESE OXIDES; PHASE DIAGRAMS; SOLID SOLUTIONS; SPECIFIC HEAT; STRONTIUM OXIDES; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0013-0065 K; TEMPERATURE RANGE 0065-0273 K; TEMPERATURE RANGE 0273-0400 K; VALENCE
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; CHALCOGENIDES; DIAGRAMS; DISPERSIONS; ELECTRIC CONDUCTIVITY; ELECTRICAL PROPERTIES; HOMOGENEOUS MIXTURES; INFORMATION; LANTHANUM COMPOUNDS; MANGANESE COMPOUNDS; MIXTURES; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; RARE EARTH COMPOUNDS; SOLUTIONS; STRONTIUM COMPOUNDS; TEMPERATURE RANGE; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT COMPOUNDS
Optional Information
- Notes
- 18 refs., 4 figs., 1 tab.