Long-term corrosion/oxidation studies under controlled humidity conditions

Independent of thermal loading scenarios, the waste packages at the potential repository at Yucca Mountain, Nevada will be exposed to environmental conditions where there is the possibility of significant water film formation occurring on the waste packages. Water films can cause aggressive aqueous film electrochemical corrosion on susceptible metals or alloys. Water film formation will be facilitated when relative humidities are high, when hygroscopic salts are present on the surfaces, when corrosion products are hygroscopic, and when particles form crevices with the surfaces (capillary effect). Also certain gaseous contaminants, such as, NOx and SO2, can facilitate water film formation. It should be noted that water film formation can occur at isolated spots (e.g. surface defects and salt particles) and need not cover the entire surface for electrochemical corrosion to occur. This activity will characterize the long term corrosion of metal specimens at two nominal relative humidities (50 and 85%) and at 80 C. Under the low relative humidity (50%) condition, water film formation is expected to be limited and therefore aqueous film electrochemical corrosion is expected also to be limited. Under the high relative humidity (85%) condition, significant water film formation is expected to occur under some test conditions, and subsequently aqueous film electrochemical corrosion will occur on susceptible materials