Studies on the electrical properties of reactive DC magnetron-sputtered indium-doped silver oxide thin films: The role of oxygen

Indium (∼10 at.%)-doped silver oxide (AIO) thin films have been prepared on glass substrates at room temperature (300 K) by reactive DC magnetron sputtering technique using an alloy target made of pure (99.99%) silver and indium (90:10 at.%) metals. The oxygen flow rates have been varied in the range 0.00-3.44 sccm during sputtering. The X-ray diffraction data on these indium-doped silver oxide films show polycrystalline nature. With increasing oxygen flow rate, the carrier concentration, the Hall mobility and the electron mean free path decrease. These films show a very low positive temperature coefficient of resistivity ∼3.40x10-8 ohm-cm/K. The work function values for these films (measured by Kelvin probe technique) are in the range 4.81-5.07 eV. The high electrical resistivity indicate that the films are in the island state (size effects). Calculations of the partial ionic charge (by Sanderson's theory) show that indium doping in silver oxide thin films enhance the ionicity