Torsional cycling of cold pressure welded zirconium/steel-specimens

Creators

  • 1. Technische Univ. Braunschweig (F.R. Germany). Inst. fuer Werkstoffkunde und Herstellungsverfahren
  • 2. Technische Univ. Braunschweig (F.R. Germany). Inst. fuer Schweisstechnik und Werkstofftechnologie

Description

Plastic fatigue (low-cycle fatigue) in cold-pressed welded zirconium/steel samples was investigated using torsional loading tests. To determine the lifespan under plastic fatigue, the critical load cycle number N Kr was used instead of the fracture load cycle number N B. N Kr is the load cycle number at which cracks occur that significantly weaken the sample. The relationship N . Δγ = C was also established for welded samples. The results were correlated with observations from unwelded samples to predict the lifespan of the welded samples. Microscopic examinations revealed crack initiation at sites of intense sliding in zirconium. Fracture consistently occurred outside the weld seam in zirconium.

Abstract (German)

Plastoermüdung (low‐cycle fatigue) an kaltpreßgeschweißten Zirkonium/Stahl‐Proben wurde im Torsionswechselversuch untersucht. Zur Bestimmung der Lebensdauer bei Plastoermüdung wurde die kritische Lastspielzahl N Kr anstelle der Bruchlastspielzahl N B verwendet. N Kr ist die Lastspielzahl, bei der Risse auftreten, die die Probe merklich schwächen. Der Zusammenhang N . Δγ = C wurde auch für geschweißte Proben gewonnen. Die Ergebnisse wurden mit den Beobachtungen an ungeschweißten Proben in Zusammenhang gebracht, um die Lebensdauer der geschweißten Proben voraussagen zu können. Mikroskopische Untersuchungen zeigten die Anrißbildung an Stellen intensiver Gleitung in Zirkonium. Der Bruch erfolgte immer außerhalb der Schweißnaht im Zirkonium.

Additional details

Additional titles

Original title (German)
Torsionswechselversuch mit kaltpressgeschweissten Zirkonium/Stahl-Proben

Identifiers

DOI
10.1002/mawe.19740050205;

Publishing Information

Journal Title
Materialwissenschaft und Werkstofftechnik
Journal Volume
5
Journal Issue
2
Series
Z. Werkstofftech.
Journal Page Range
72-77
ISSN
0933-5137

INIS

Country of Publication
Germany
Country of Input or Organization
Germany
INIS RN
5127000
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
BONDING; COLD PRESSING; CRACKS; FAILURES; FATIGUE; FRACTURES; MATERIALS TESTING; MICROSTRUCTURE; SLIP; STAINLESS STEEL-304; STRAINS; STRESSES; TIME DEPENDENCE; TORSION; WELDED JOINTS; WELDING; ZIRCONIUM
Descriptors DEC
ALLOYS; CHROMIUM ALLOYS; CHROMIUM-NICKEL STEELS; CORROSION RESISTANT ALLOYS; CRYSTAL STRUCTURE; ELEMENTS; FABRICATION; HEAT RESISTING ALLOYS; IRON ALLOYS; IRON BASE ALLOYS; JOINING; JOINTS; MATERIALS WORKING; MECHANICAL PROPERTIES; METALS; NICKEL ALLOYS; PRESSING; STAINLESS STEELS; STEELS; TESTING; TRANSITION ELEMENTS

Optional Information

Notes
9 tabs.; 1 fig.; 8 refs.; Updated automatically by Metadata and Full-Text Enrichment Agent