Trapped field measurements on MgB₂ bulk samples

Trapped field measurements were performed on bulk, polycrystalline MgB₂ samples stemming from different sources with the emphasis to develop applications like superconducting permanent magnets ('supermagnets') and electric motors. We describe the setup for the trapped field measurements and the experimental procedure (field cooling, zero-field cooling, field sweep rates). The trapped field measurements were conducted using a cryocooling system to cool the bulk samples to the desired temperatures, and a low-loss cryostat equipped with a room-temperature bore and a maximum field of ±5 T was employed to provide the external magnetic field. The superconducting coil of this cryostat is operated using a bidirectional power supply. Various sweep rates of the external magnetic field ranging between 1 mT/s and 40 mT/s were used to generate the applied field. The measurements were performed with one sample and two samples stacked together. A maximum trapped field of 7 T was recorded. We discuss the results obtained and the problems arising due to flux jumping, which is often seen for the MgB₂ samples cooled to temperatures below 10 K.