Effect of DCCA on synthesis of inorganic mesoporous gels

Full text.The porous texture of the monolith inorganic gels plays an important role in the utilization of porous material by control of several properties such as gas diffusion, thermal stability, mechanical strength. the sol gel process provides many possibilities to manufacture porous material with extremely low concentration of impurities at low sinter temperature. The serious problem in the production of the monolith gels is fracture and crack formation which may occur in the conversion of the wet gels to dry gels. This phenomenon is probably due to the capillary forces which appear during the drying steps. in order to reduce the effect of capillary forces a number of methods were applied (hyper critic drying, organic DCCAs). The purpose of the present work, is to understand the chemical changes that result from adding formamide as drying control chemical additives DCCA to the colloidal silica sols in the presence of acid catalyst. Fourier Transformed Infrared spectroscopy and Raman spectroscopy were used to investigate the influence of formamide on gel formation. The Nitrogen adsorption-desorption technique is used to investigate the effect of formamide on gel texture. The results show that the gels with formamide are monolith and obtained during a short time of gelling reaction, the silica particles link formation depend strongly on the formamide concentration. the BET and BJH results show that the presence of formamide promotes the creation of meso porous texture depending on formamide/silica molar ratio in the starting sol. The maximum average diameter of the obtained gel reaches a value close to 25 nm with a bulk density equal to 1.1 g/cm3