Production of wood plastic properties using gamma radiation as a polimerization agent

The properties of wood plastic composites (WPC) based on Pinus Radiata D. Don impregnated with methylmethacrylate and subsequently polymerized with gamma radiation were studied. Different systems of impregnation were utilized, in order to obtain partial and shell loads. The minimum irradiation dose uses was 16 kGy. The following tests were made to the material: static bending, compression strenght parallel to grain, hardness, sheer strength, toughness, water absorption, dimensional stability and flame propagation index. To evaluate the testing, the results of the samples were separated according final density in the ranges: R1 = 429-483 kg/m3 (without treatment); R2 = 500-650 kg/m3 and R3 = 651-850 kg/m3. In general, the best results were obtained for samples of high density. The most important results were achieved for dimensional stability, water absorption and hardness. (Author)