Strength and creep of structural materials based on intermetallic compound NiAl

Creators

  • 1. Moskovskij Gosudarstvennyj Inst. Stali i Splavov (Tekhnologicheskij Univ.), Moscow (Russian Federation)

Description

Hot strength and short-term creep resistance are studied for composite materials with a honeycomb structure obtained from Mo or W coated NiAl, NiAl + Hf or NiAl + Nb powder particles by compacting. It is shown that Mo and W deposition on powder particle surfaces results in an increase of hot strength, creep resistance and plasticity in a temperature range of 1000-1300 deg C. The plasticity is highest for a NiAl + W composite material. With a growth of compression test temperature from 1000 to 1300 deg C the efficiency of solid solution hardening of NiAl with hafnium reduces and the efficiency of hardening due to a honeycomb structure increases

Abstract (Russian)

Исследовали горячую прочность и сопротивление кратковременной ползучести в композитных материалах с сотовой структурой, полученных компактированием частиц NiAl, NiAl + Hf или NiAl + Nb, предварительно покрытых Mo или W. Показано, что осаждение Mo или W на поверхность частиц порошка приводит к увеличению горячей прочности, сопротивления ползучести и пластичности в диапазоне температур 1000-1300 град С. Пластичность максимальна для композиции NiAl + W. С ростом температуры испытаний на сжатие от 1000 до 1300 град С эффективность твердорастворного упрочнения NiAl гафнием снижается, а эффективность упрочнения за счет сотовой структуры возрастает

Additional details

Additional titles

Original title (Russian)
Прочность и ползучесть конструкционных материалов на основе интерметаллида NiAl

Publishing Information

Journal Title
Fizika Metallov i Metallovedenie
Journal Volume
101
Journal Issue
4
Journal Page Range
p. 429-435
ISSN
0015-3230
CODEN
FMMEA9

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
37070164
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ALUMINIUM ALLOYS; CHEMICAL COMPOSITION; COMPACTS; COMPOSITE MATERIALS; COMPRESSION STRENGTH; CREEP; GRANULAR MATERIALS; HAFNIUM ADDITIONS; INTERMETALLIC COMPOUNDS; MICROSTRUCTURE; MOLYBDENUM; NICKEL ALLOYS; NIOBIUM ADDITIONS; PARTICLE SIZE; PHYSICAL VAPOR DEPOSITION; POWDERS; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 1000-4000 K; TUNGSTEN
Descriptors DEC
ALLOYS; DEPOSITION; ELEMENTS; HAFNIUM ALLOYS; MATERIALS; MECHANICAL PROPERTIES; METALS; NIOBIUM ALLOYS; REFRACTORY METALS; SIZE; SURFACE COATING; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS; TRANSITION ELEMENTS

Optional Information

Notes
6 refs., 4 figs., 4 tabs.