The present Ni-Zn ferrite magnetic properties sensitive to microstructure and obtain a ferrite with a uniform microstructure is the biggest challenge in the advancement of new technologies. This study proposes to evaluate the microstructure and magnetic properties of Ni-Zn ferrite sintered by microwave energy. The samples were previously synthesized by combustion reaction using urea and glycine, with 1200 deg C/2h sintered at a heating rate of 5 deg C/min, and characterized by density, XRD, SEM and magnetic measurements. The results show that the sample synthesized with glycine showed the formation of ferrite phase and traces of secondary phase hematite, grains with undefined format, and a high porosity and inter intragranular. The sample synthesized with urea gave only the ferrite phase, with hexagonal grains, and low intergranular porosity. The sample synthesized with urea showed better magnetic characteristics when compared with the samples synthesized with glycine. (author)