Kinetics of crack growth in cast turbine vessel parts during operation
Creators
- 1. Vserossijskij Teplotekhnicheskij Inst., Moscow (Russian Federation)
Description
It is shown in the result of comparing the kinetic equations of the 15Kh1M1FL steel under creep conditions at 540 deg C, obtained by the samples testing, that the fracture growth rate may be determined through the ratios of the linear destruction mechanics with application of the strain intensity coefficient. The prospects for application of the new equation, making it possible to account for the temperature effect on the fracture growth rate for processing the experimental data through the fracture growth rate in the 15Kh1M1FL steel, obtained within the range of 510-565 deg C, are also noted. The recommendations on the size of fractures, which may be left in the high-temperature vessel details for the intermaintenance period, are presented
Abstract (Russian)
В результате сравнения кинетических уравнений ползучести при 540 град. С стали 15Х1М1ФЛ, полученных путем испытания образцов, показано, что скорость роста трещины может быть достаточно успешно определена с помощью соотношений линейной механики разрушения с применением коэффициента интенсивности напряжений. Кроме того, отмечена перспективность использования нового уравнения, позволяющего учитывать влияние температуры на скорость роста трещины для обработки экспериментальных данных по скорости роста трещины в стали 15Х1М1ФЛ, полученных в диапазоне 510-565 град. С. Даны рекомендации по величине трещин, которые можно оставлять в высокотемпературных корпусных деталях на межремонтный срокAdditional details
Additional titles
- Original title (Russian)
- Кинетика роста трещин на литых деталях турбин в процессе эксплуатации
Publishing Information
- Journal Title
- Teploehnergetika
- Journal Issue
- no.4
- Journal Page Range
- p. 22-26
- ISSN
- 0040-3636
- CODEN
- TPLOA5
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 32010470
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CRACK PROPAGATION; CREEP; FRACTURE MECHANICS; IMPACT STRENGTH; KINETIC EQUATIONS; STEEL-CRMOV; STRESS INTENSITY FACTORS; TEMPERATURE RANGE 0400-1000 K; TENSILE PROPERTIES; TURBINES
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CHROMIUM ALLOYS; COPPER ADDITIONS; COPPER ALLOYS; EQUATIONS; EQUIPMENT; IRON ALLOYS; IRON BASE ALLOYS; LOW ALLOY STEELS; MACHINERY; MECHANICAL PROPERTIES; MECHANICS; MOLYBDENUM ADDITIONS; MOLYBDENUM ALLOYS; NICKEL ADDITIONS; NICKEL ALLOYS; STEELS; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS; TURBOMACHINERY; VANADIUM ADDITIONS; VANADIUM ALLOYS
Optional Information
- Notes
- 7 refs., 2 figs., 3 tabs.