Comparative biomechanical study between fresh frozen bone and fresh frozen pasteurized bone process

To observe the biomechanical properties difference between fresh frozen bone and fresh frozen pasteurized bone process Thirty eight femurs bones taken from 6 years old primate.(macaca fascicularis) from Primate Nursery Center LIPI Bogor, 20 bones were 6 cm cut for bending test and 18 remains were 3 cm cut for compression test. All bones were frozen and then divided into two groups for each biomechanical study. First group (I 0 bones for bending test and 9 bones for compression test) were undergone fresh frozen procession only. The second group with the same amount was undergone fresh frozen and pasteurized on 60 degree C for three hours. Bending test was done until the bones were broken on control group and pasteurized group and the result was compared, the same procedure was done for compression test. The study was done in room temperature. The biomechanical test result was analyzed by two independent T tests. The bending test control group has ( mean 0.097 N / mm sup 2 (SD = 0.007) and the pasteurized group ( mean 0. I 0 1 N / mm sup 2 (SD = 0.0 1 3), there was no significant difference (p 0.399). The compression test control group has ( = mean 0.71 N / mm sup 2 (SD=0.128)where as the pasteurized group has(mean 0.50N/mm sup 2 (SD=0.111),there was significant difference (p =0.004) From the result biomechanical study on bending test, there was no significant difference of bone strength, whereas on compression test the fresh frozen with pasteurized bone group is 125% stronger than control group. The result of this study will be very useful for reconstruction bone allograft