Further Charpy impact test results of low activation ferritic alloys, irradiated at 430 degrees C to 67 dpa
Creators
- 1. Pacific Northwest National Lab., Richland, WA (United States)
Description
Miniature CVN specimens of four ferritic alloys, GA3X, F82H, GA4X and HT9, have been impact tested following irradiation at 430 degrees C to 67 dpa. Comparison of the results with those of the previously tested lower dose irradiation condition indicates that the GA3X and F82H alloys, two primary candidate low activation alloys, exhibit virtually identical behavior following irradiation at 430 degrees C to ∼67 dpa and at 370 degrees C to ∼15 dpa. Very little shift is observed in either DBTT or USE relative to the unirradiated condition. The shifts in DBTT and USE observed in both GA4X and HT9 were smaller after irradiation at 430 degrees C to ∼67 dpa than after irradiation at 370 degrees C to ∼15 dpa
Files
Restricted
The record is publicly accessible, but files are restricted to users with access.
Additional details
Publishing Information
- Imprint Title
- Fusion materials semiannual progress report for the period ending December 31, 1996
- Imprint Pagination
- 296 p.
- Journal Page Range
- p. 151-155.
- Report number
- DOE/ER--0313/21
INIS
- Country of Publication
- United States
- Country of Input or Organization
- United States
- INIS RN
- 29021890
- Subject category
- S36: MATERIALS SCIENCE; S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Progress Report
- Descriptors DEI
- CHARPY TEST; FERRITIC STEELS; PHYSICAL RADIATION EFFECTS; PROGRESS REPORT; TEMPERATURE RANGE 0400-1000 K
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; DESTRUCTIVE TESTING; DOCUMENT TYPES; IMPACT TESTS; IRON ALLOYS; IRON BASE ALLOYS; MATERIALS TESTING; MECHANICAL TESTS; RADIATION EFFECTS; STEELS; TEMPERATURE RANGE; TESTING; TRANSITION ELEMENT ALLOYS
Optional Information
- Contract/Grant/Project number
- Contract AC06-76RL01830