A non-thermal chemical synthesis of hydrophilic and amorphous cobalt oxide films for supercapacitor application

Present work explored a room temperature, simple and low cost chemical route for the preparation of hydrophilic cobalt oxide films from alkaline cobalt chloride (CoCl2:6H2O) and double distilled water precursor solutions. As-deposited cobalt oxide films showed amorphous nature, which is one of the prime requirements for supercapacitor, as confirmed from X-ray diffraction studies. Changes in direct band gap energy and electrical resistivity of as-deposited cobalt oxide films were confirmed after annealing. Spherical grains of about 40-50 nm diameters were uniformly distributed over the substrate surface. Surface wettability studied in contact with liquid interface, showed hydrophilic nature as water contact angle was <90o. Finally, presence of cobalt-oxygen covalent bond was observed from Raman shift experiment