Formation enthalpy of alkali-borosilicate glass

Creators

  • 1. AN SSSR, Leningrad (Russian Federation). Inst. Khimii Silikatov

Description

Temperature dependence of formation enthalpy of glass of the composition 0.0438Na2O-0.0385K2O-0.3394B2O3-0.5783SiO2 was determined using the method of high-temperature colorimetry-dissolution, mixing and differential scanning calorimetry. The glass considered has liquation nature-two-vitrification ranges at 713 K and 817 K are detected. The brightening point is 922 K. The calculation of formation enthalpy using the method of partial heat capacities is made in the temperature range of 973-1473 K. Formation enthalpy does not depend on temperature in the temperature range of 298-1273 K

Additional details

Additional titles

Original title (Russian)
Энтальпия образования щелочноборосиликатного стекла

Publishing Information

Journal Title
Fizika i Khimiya Stekla
Journal Volume
17
Journal Issue
6
Journal Page Range
p. 951-953.
ISSN
0132-6651
CODEN
FKSTD5

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
24049503
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ALKALI METAL COMPOUNDS; BOROSILICATE GLASS; CHEMICAL COMPOSITION; FORMATION HEAT; PHASE TRANSFORMATIONS; SPECIFIC HEAT; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0400-1000 K; TEMPERATURE RANGE 1000-4000 K
Descriptors DEC
ENTHALPY; GLASS; PHYSICAL PROPERTIES; REACTION HEAT; TEMPERATURE RANGE; THERMODYNAMIC PROPERTIES