Influence of corrosive impurities in the irradiation of fuel elements for high-temperature reactors

Creators

Description

Automatic translation: The spherical fuel elements for high-temperature reactors are exposed to corrosion during reactor operation. At extreme Load are on the matrix of BE from the irradiation experiments and corrosive changes have been detected by the AVR. Additional loads after the irradiation could prevent the corrosion be made clear. Theoretical considerations on the corrosion process are given. The available data on the fuel elements from the experiments have been compiled and evaluated. The evaluations revealed the following relationships. High irradiation temperature promotes corrosion. Matrix impurities (Fe, Mo) support the oxidation process catalytically. Large doses of radiation can make the elements more resistant to corrosion. High final annealing temperatures reduce corrosion rates. A significant influence of cooling gas contamination, uranium contamination and fission products on the corrosion behavior of the fuel assembly could not be proven.

Abstract (German)

Die kugelförmigen Brennelemente für Hochtemperaturreaktoren sind während des Reaktorbetriebes der Korrosion ausgesetzt. Bei extremer Belastung sind an der Matrix der BE aus den Bestrahlungsexperimenten und vom AVR korrosive Veränderungen festgestellt worden. Durch zusätzliche Belastungen nach der Bestrahlung konnte die Korrosion deutlich gemacht werden. Theoretische Überlegungen zu dem Korrosionsvorgang sind angegeben. Die verfügbaren Daten über die Brennelemente aus den Experimenten sind zusammengestellt und ausgewertet worden. Die Auswertungen ließen die folgenden Zusammenhänge erkennen. Hohe Bestrahlungstemperatur wirkt korrosionsfördernd. Matrixverunreinigungen (Fe, Mo) unterstützen katalytisch den Oxydationsvorgang. Große Bestrahlungsdosen können die Elemente korrosionsbeständiger machen. Hohe Endglühtemperaturen reduzieren die Korrosionsraten. Ein wesentlicher Einfluß von Kühlgasverunreinigungen, Urankontaminationen und Spaltprodukten auf das Korrosionsverhalten der BE konnte nicht belegt werden.

Files

Restricted

The record is publicly accessible, but files are restricted to users with access.

Additional details

Additional titles

Original title (German)
Einfluß korrosiv wirkender Verunreinigungen bei der Bestrahlung von Brennelementen für Hochtemperaturreaktoren

Publishing Information

Imprint Pagination
141 p.
Report number
INIS-DE--22M0850

INIS

Country of Publication
Germany
Country of Input or Organization
International Atomic Energy Agency (IAEA)
INIS RN
54017921
Subject category
S21: SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS;
Resource subtype / Literary indicator
Thesis
Descriptors DEI
CORROSION; EVALUATION; FEDERAL REPUBLIC OF GERMANY; FISSION PRODUCTS; FORSCHUNGSZENTRUM JUELICH; FUEL ASSEMBLIES; FUEL ELEMENTS; HTGR TYPE REACTORS; IRRADIATION; REACTOR OPERATION; TEMPERATURE RANGE 0400-1000 K; URANIUM
Descriptors DEC
ACTINIDES; CHEMICAL REACTIONS; DEVELOPED COUNTRIES; ELEMENTS; EUROPE; GAS COOLED REACTORS; GERMAN FR ORGANIZATIONS; GRAPHITE MODERATED REACTORS; ISOTOPES; MATERIALS; METALS; NATIONAL ORGANIZATIONS; OPERATION; RADIOACTIVE MATERIALS; REACTOR COMPONENTS; REACTOR LIFE CYCLE; REACTORS; TEMPERATURE RANGE; WESTERN EUROPE

Optional Information

Notes
44 refs., 43 figs., 42 tabs.