Radiation degradation of alginate and chitosan

Alginate and chitosan were irradiated in solid or aqueous solution condition with Co60 gamma rays in the dose range of 20 to 500 kGy. Degradation was observed both in solid and solution conditions. The degradation in solution was remarkably greater than that in solid. For example, the molecular weight of alginate in 4%(w/v) solution decreased from 2 x 105 for 0 kGy to 6 x 103 for 50 kGy irradiation while the equivalent degradation by solid irradiation required 500 kGy. The activated species from irradiated water must be responsible for the degradation in solution. The degradation was also accompanied with the color change of alginate: the color became deep brown for highly degraded alginate. UV spectra showed a distinct absorption peak at 265 nm for colored alginates, increasing with dose. The fact that discoloration of colored alginate was caused on exposure to ozone suggests a formation of double bond in pyranose-ring by scission of glycosidic bond. Degradation behavior of chitosan in irradiation was almost the same as that of alginate. (author)