Characteristics of the Li⁺-Ion Conductivity of Li₃R₂(PO₄)₃ Crystals (R = Fe, Sc) in the Superionic State

The characteristics of Li+-ion conductivity σdc of structural γ modifications of Li₃R₂(PO₄)₃ compounds (R = Fe, Sc) existing in the superionic state have been investigated by impedance spectroscopy. The type of structural framework [R₂P₃O₁₂]_∞^3- affects the σdc value and the σdc activation enthalpy in these compounds. The ion transport activation enthalpy in γ-Li₃R₂(PO₄)₃ (ΔH_σ = 0.31 ± 0.03 eV) is lower than in γ-Li₃Fe₂(PO₄)₃ (ΔH_σ = 0.36 ± 0.03 eV). The conductivity of γ-Li₃Fe₂(PO₄)₃ (σ_dc = 0.02 S/cm at 573 K) is twice as high as that of γ-Li₃R₂(PO₄)₃. A decrease in temperature causes a structural transformation of Li₃R₂(PO₄)₃ from the superionic γ modification (space group Pcan) through the intermediate metastable β modification (space group P2₁/n) into the "dielectric" α modification (space group P2₁/n). Upon cooling, σdc for both phosphates decreases by a factor of about 100 at the superionic TSIC transition. In Li₃Fe₂(PO₄)₃ σdc gradually decreases in the temperature range T_SIC = 430–540 K, whereas in Li₃R₂(PO₄)₃ σdc undergoes a jump at T_SIC = 540 ± 25 K. Possible crystallochemical factors responsible for the difference in the σdc and ΔH_σ values and the thermodynamics and kinetics of the superionic transition for Li₃R₂(PO₄)₃ are discussed.