Protoporphyrin-IX conjugated cellulose nanofibers that exhibit high antibacterial photodynamic inactivation efficacy

Towards the development of anti-infective nanoscale materials employing a photodynamic mechanism of action, we report the synthesis, physical properties (SEM, mechanical strength, water contact angle), spectroscopic characterization (infrared, Raman, DRUV), and evaluation of antibacterial efficacy of porphyrin-conjugated regenerated cellulose nanofibers, termed RC-TETA-PPIX-Zn. Cellulose acetate was electrospun to produce nanofibers, thermally treated to enhance mechanical strength, and finally hydrolyzed to produce regenerated cellulose (RC) nanofibers that possessed a high surface area and nanofibrous structure. Covalent grafting of a protoporphyrin IX (PPIX) photosensitizer using epichlorohydrin/triethylenetetramine (TETA), followed by zinc chelation, afforded RC-TETA-PPIX-Zn. The high surface area afforded by the nanofibers and efficient photosensitizer conjugation led to a very high loading of 412 nmol PPIX/mg material, corresponding to a degree of substitution of 0.1. Antibacterial efficacy was evaluated against Staphylococcus aureus (ATCC-6538) and Escherichia coli (ATCC-8099), with our best results achieving detection limit inactivation (99.999+%) of both bacteria after only 20 min illumination (Xe lamp, λ ≥ 420 nm). No statistically significant loss in antibacterial activity was observed when using nanofibers that had been 'photo-aged' with 5 h of pre-illumination to simulate the effects of photobleaching. Post aPDI, scanning electron microscopy revealed that the bacteria had undergone cell membrane leakage, consistent with oxidative damage caused by photo-generated reactive oxygen species. Taken together, the conjugation strategy employed here provides a scalable, facile and efficient route to creating nanofibrous materials from natural polymers with a high photosensitizer loading, enabling the use of commercially-available neutral porphyrin photosensitizers, such as PPIX, in the design and synthesis of potent anti-infective nanomaterials. (paper)