Materials problems related to the core catcher of sodium cooled reactors

There are in principal two possible solutions for the external core catcher as far as materials are concerned. 1) A barrier consisting of a material with a high melting point, 2) a tray of comparatively low melting material with a high solubility for the fuel. In case of the first concept one has to look for materials whose melting temperatures are above the temperature of the molten core. Based on metallurgical reasons it seems very likely that the molten core does not exceed a temperature in the range between 2,500 and 2,8000C. Due to the compatibility situation with the molten core only a few high melting oxides will be suitable as liner materials for a core catcher. In the second case basalt or concrete, if free of water and lime, are suitable materials. Graphite is a high melting material, however, due to its behaviour with the molten core it should be listed under the second group. By the reaction of graphite with the core materials the melt can be kept liquid down to temperatures of around 1,1000C. The evolution of CO by this reaction should be supportable. It is an endothermal reaction. Experiments on the behaviour of core catcher materials have shown that sodium is capable of penetrating into sintered bodies of UO2 with densities of 90% TD at temperatures higher than 2000C. This may lead to the desintegration of these bodies. The exposure to moist air has not done much harm to UO2 pellets of densities from 80 to 90% TD. Even after one year of exposure, swelling or desintegration could not be observed. Sodium is also capable of penetrating into bodies of synthetic carbon and graphite. Only well graphitized material will not be destroyed. (orig.)