Thickness measurement for the different metals by using Cs-137 gamma source with gamma transmission technique

The purpose of this study is an experimental analysis of thickness measurement for various metals with the gamma transmission technique using Cs-137 as the radioisotope source. Lead, steel, brass, and aluminum, which are frequently used metals in industry, were chosen for the experiments. As the radioisotope source Cs-137 was preferred for the study since it has long half-life, it is mono energetic, and it penetrates the metals that were studied. Experiments were observed in the constant experimental geometry. Calibration curves for the four metal samples were plotted using the obtained results. To test the plotted calibration curves, counts for determining thickness measurement were collected for each sample and the obtained relative count values were used in conjunction with the plotted calibration curves for each sample to determine its thickness. The thicknesses of the samples have been measured with a micrometer and the results were comparatively analyzed with the measurement results obtained by the gamma transmission technique. The results of the analyses revealed that the thickness measurement values obtained with the gamma transmission technique and the thickness measurement values obtained with the conventional technique significantly converge to each other and the difference between the two values is at an acceptable level. Therefore the reliability of thickness measurements with the gamma transmission technique and the resulting calibration curves have been demonstrated.