Effect of discontinuities as a means to alleviate thermal expansion mismatch damage in laminar composites

An investigation of Nichrome/tungsten laminar composites showed that intentionally introduced discontinuities, such as perforations through or grooves on the surface of the matrix laminae, improved thermal expansion mismatch damage resistance. It was found that specimens having smooth matrix laminate surfaces were virtually destroyed by delamination in 21 or fewer fast cool cycles in which they were water quenched from 981 C. Specimens having interior matrix laminae with discontinuities and relatively thin, nondiscontinuous, surface matrix laminae resisted 50 similar cycles without evident delamination damage