Biodegradable aliphatic-aromatic copolyester/corn starch blend composite reinforced with coffee parchment husk

In recent years, studies have shown that the addition of natural fiber or proper filler is an effective strategy for achieving improved properties in biodegradable polymer materials. Moreover, is especially important if such fibers are residues of agro-industrial processes. In this work, a promising technique to develop biodegradable polymer matrix composite based on aliphatic-aromatic copolyester/corn starch blend (Evela®) and coffee parchment husk, which is residue from coffee processing is described. The biodegradable polymeric blend (Evela®) with 5 % (w/w) of ball-milled coffee parchment husk fiber powder, with size ≤250 μm, without any modification was prepared by melt-mixing processing, using a twin screw extruder machine and then pelletized. In a second step, the pelletized Evela®)/coffee parchment (Composite) was then dried at 70 ± 2 deg C for 24 h in a circulating air oven, fed into injection molding machine and test specimens were obtained. The Composite specimen samples were irradiated using an electron beam accelerator, at radiation dose of 20 and 40 kGy, at room temperature in presence of air. The irradiated and non-irradiated samples were characterized by means of scanning electron microscopy (SEM), X-Ray diffraction (XRD), tensile tests and sol-gel analysis and the correlation between their properties was discussed. In addition, coffee parchment husk fiber characterization by SEM, EDS, XRD and WDXRF have also been carried out with a view to evaluate its importance in determining the end-use properties of the composite. (author)