Bright, water-soluble CeF₃ photo-, cathodo-, and X-ray luminescent nanoparticles

Bright, water-soluble CeF₃ nanoparticles with small size and narrow size distribution have been synthesized using a simple co-precipitation method without any ligands. Size control of nanoparticles from 13 ± 2 to 9 ± 2 nm was achieved by varying the reaction time. Colloidal properties have been found to vary with pH and, independently, with dilution. The photoluminescence of the as-synthesized nanoparticles shows a highly photostable UV/Visible fluorescence band due to allowed 5d–4f transitions, also observed in the X-ray luminescence spectrum. This band is suitable for X-ray excitation of a range of photosensitizers. The photoluminescence quantum yield of nanoparticles was also determined to be 31 %. Using the measured fluorescence decay time of 25 ns, the radiative lifetime of Ce in CeF₃ was found to be 80.6 ns. Both photoluminescence and cathodoluminescence emission are affected by the reaction time and measurement temperature. Electron-beam-induced defect annealing is also observed