Direct observations of the primary state of radiation damage of ion-irradiated tungsten and platinum

A brief summary was presented of all the Cornell work on the primary state of radiation damage in ion-irradiated tungsten and platinum. The primary research tool for all this research was the field-ion microscope (FIM); the FIM was ideally suited for this research because of its excellent atomic resolution and the ability to examine the interior of the specimens, as a result of the field-evaporation effect. This paper summarized, in outline form, the following items: (1) the principal experimental quantities determined from the analyses performed on all the individual depleted zones (DZs) observed; (2) the main experimental programs; (3) a number of the more important results and conclusions concerning the vacancy structure of DZs; and (4) the three-dimensional spatial distribution of self-interstitial atoms around DZs in tungsten which had been irradiated and examined in situ at 100K