Analysis of local regions near the interfaces in nanostructured multicomponent cathodic – arc – vapor – deposition (CAVD) coatings (Ti-Zr-Hf-V-Nb)N

Multicomponent, nanostructure (Ti- Zr-Hf-V-Nb)N coatings derived using cathodic – Arc – Vapor – Deposition method, were characterized by applying SPB, (μ-PIXE), EDS and SEM-analysis), XRD methods, including ''a-sin²φ'' procedure. It was found that through the creation of high elastic strains of compression in coating it is possible to a significant extent enhance its oxidation resistance under high-temperature annealing. During the characterization of coatings the elements and defects’ redistribution was discovered, its segregation through thermally-stimulated diffusion and the spinoidal segregation process end, in the neighborhood of the interfaces, around grains and subgrains, without substantial change of the average nanograin dimension. (authors)