Research on modulated structure alloys

Research was carried out for the purposes of clarifying the cause of modulated structure formation, developing the structure control method utilizing modulated structure and clarifying the suitability of modulated structure alloys as radiation damage-resisting materials. The research on structure control method encountered a difficulty in the analysis of experimental results, bu the following results were obtained in the other items. The method of solving a diffusion equation including a nonlinear term was found in course of the clarification of the cause of modulated structure formation. As a means of detecting faint unevenness in solid solution, of which the deviation of composition is a few %, the structure analysis method utilizing magnetic property was developed. This method was applied to Ni-9.6 at.% Ti alloy, and the process of expanding amplitude in composition variation in spinodal decomposition and the formation of solute atomshort region at the time of nucleation-growth were confirmed. Utilizing the high energy electron beam generated in a superhigh voltage electron microscope, electron beam irradiation experiment was carried out on precipitation hardening alloys with modulated structure. As the result, it was found that in Ni-Ti alloy, the amount of void swelling resistance showed the change with the increase of modulated structure period. (Kako, I.)