NdBa2Cu3Oz Superconducting phase evolution during isothermal annealing

Creators

  • 1. Moskovskij Gosudarstvennyj Univ. im. M.V. Lomonosova, Moscow (Russian Federation)

Description

By means of X-ray phase analysis, differential scanning calorimetry, thermogravimetric analysis and by measuring of specific magnetic susceptibility one investigated systematically into variation of superconducting properties of NdBa2Cu3Oz phase depending on temperature (760-1000 deg C) and duration (1-100 h) of isothermal annealing in air and plotted time-temperature-transformation diagram (TTT-diagram). Annealing of the initial reagents at fewer than 900 deg C temperature in air and formation of intermediate metastable phases with disordering of barium and neodymium cations are shown to be the most essential reasons causing deterioration of superconducting properties of neodymium cuprate. Long-term (50-100 h) annealing and 950-1000 deg C temperatures allow producing NdBa2Cu3Oz cation-ordered structure

Abstract (Russian)

Методами рентгенофазового анализа, дифференциальной сканирующей калориметрии, термогравиметрического анализа и измерением удельной магнитной восприимчивости систематически исследованы изменения сверхпроводящих свойств фазы NdBa2Cu3Oz в зависимости от температуры (760-1000 град С) и продолжительности (1-100 ч) изотермического отжига на воздухе, и построена диаграмма время-температура-превращение (ТТТ-диаграмма). Показано, что одной из основных причин ухудшения сверхпроводящих свойств купрата неодима является отжиг исходных реагентов при температуре ниже 900 град С на воздухе и формирование промежуточных метастабильных фаз с разупорядочением катионов бария и неодима. При длительном (50-100 ч) отжиге и температурах 950-1000 град С достигается катионно-упорядоченная структура NdBa2Cu3Oz

Additional details

Additional titles

Original title (Russian)
Эволюция сверхпроводящей фазы NdBa

Publishing Information

Journal Title
Doklady Akademii Nauk - Rossijskaya Akademiya Nauk
Journal Volume
383
Journal Issue
5
Journal Page Range
p. 651-656
ISSN
0869-5652
CODEN
DAKNEQ

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
35001600
Subject category
S36: MATERIALS SCIENCE; S37: INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY;
Descriptors DEI
AIR; BARIUM COMPOUNDS; CHEMICAL PREPARATION; CUPRATES; DIAGRAMS; HEAT TREATMENTS; HIGH-TC SUPERCONDUCTORS; NEODYMIUM COMPOUNDS; PHASE STUDIES; PHASE TRANSFORMATIONS; SUPERCONDUCTIVITY; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 1000-4000 K; TIME DEPENDENCE
Descriptors DEC
ALKALINE EARTH METAL COMPOUNDS; COPPER COMPOUNDS; ELECTRIC CONDUCTIVITY; ELECTRICAL PROPERTIES; FLUIDS; GASES; INFORMATION; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; RARE EARTH COMPOUNDS; SUPERCONDUCTORS; SYNTHESIS; TEMPERATURE RANGE; TRANSITION ELEMENT COMPOUNDS; TYPE-II SUPERCONDUCTORS

Optional Information

Notes
12 refs., 4 figs.