In this paper, Al2O3–SiC composites were produced by SPS at temperatures of 1600°C for 10min under vacuum atmosphere. For preparing samples, Al2O3 with the second phase including of micro and nano-sized SiC powder were milled for 5h. The milled powders were sintered in a SPS machine. After sintering process, phase studies, densification and mechanical properties of Al2O3–SiC composites were examined. Results showed that the specimens containing micro-sized SiC have an important effect on bulk density, hardness and strength. The highest relative density, hardness and strength were 99.7%, 324.6 HV and 2329MPa, respectively, in Al2O3–20wt% SiCmicro composite. Due to short time sintering, the growth was limited and grains still remained in nano-meter scale.
Availability note (English)
Available doi: 10.1016/j.bsecv.2017.01.002Abstract (Spanish)
En este trabajo se muestran compuestos de Al2O3-SiC producidos por SPS, en vacío, a 1.600 °C durante 10 min. Para la preparación de muestras, se molieron polvos de Al2O3 durante 5 h con la segunda fase de micro-y-nano polvo de SiC. Posteriormente, estos polvos molidos se sinterizaron mediante SPS. Después del proceso de sinterización, se realizaron estudios de fase, densificación y propiedades mecánicas de los compuestos de Al2O3-SiC obtenidos. Los resultados mostraron que micro-SiC en las muestras tiene un efecto importante en su densidad aparente, dureza y resistencia. La mayor densidad relativa, dureza y resistencia fueron respectivamente del 99,7%, 324,6 HV y 2.329 MPa para Al2O3 con un 20% en peso micro-SiC. Debido al corto tiempo de sinterización, el crecimiento los granos fue limitado y se mantuvieron en escala nanométrica.Additional details
Additional titles
- Original title (Spanish)
- Producción de nano-composites – SiC–Al2O3 por spark plasma sinterizado
Identifiers
Publishing Information
- Journal Title
- Boletin de la Sociedad Espanola de Ceramica y Vidrio
- Journal Volume
- 56
- Journal Issue
- 4
- Journal Page Range
- p. 186-194
- ISSN
- 0366-3175
- CODEN
- BSCVB9
INIS
- Country of Publication
- Spain
- Country of Input or Organization
- Spain
- INIS RN
- 48089011
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CERAMICS; DENSITY; HARDNESS; MECHANICAL PROPERTIES; NANOSTRUCTURES; SINTERING
- Descriptors DEC
- FABRICATION; MECHANICAL PROPERTIES; PHYSICAL PROPERTIES