Effect of crystallization on the electrical resistance and structure of the Co67Cr7Fe4Si8B14 amorphous alloy

Creators

  • 1. Donetskij Fiziko-Tekhnicheskij Inst. im. A.A. Galkina NAN Ukrainy, Donetsk (Ukraine)

Description

By means of resistometry and X-ray diffraction analysis one investigated into evolution of electrical resistance and structure of Co67Cr7Fe4Si8B14 amorphous alloy under continuous heating with a steady rate. Alloy is shown to crystallize by the eutectic mechanism. One investigated into phase composition of crystallization products. A mixed amorphous-nanocrystalline structure is shown to be obtained within 870-920 K temperature range. On temperature dependence of electrical resistance of the basic amorphous alloy one detected anomalies at T = 497 and 843 K. Paper presents discussion of possible reasons to induce the mentioned anomalies

Abstract (Russian)

Методами резистометрии и рентгенографического анализа изучена эволюция электросопротивления и структуры аморфного сплава Co67Cr7Fe4Si8B14 при непрерывном нагреве с постоянной скоростью. Установлено, что процесс кристаллизации сплава протекает по эвтектическому механизму. Изучен фазовый состав продуктов кристаллизации. Показано, что в интервале температур 870-920 К реализуется смешанная аморфно-нанокристаллическая структура. На температурной зависимости электросопротивления исходного аморфного сплава обнаружены аномалии при Т = 497 и 843 К. Обсуждаются возможные причины их возникновения

Additional details

Additional titles

Original title (Russian)
Особенности изменения электросопротивленияи структуры в процессе кристаллизации аморфного сплава Cо

Publishing Information

Journal Title
Neorganicheskie Materialy
Journal Volume
38
Journal Issue
11
Journal Page Range
p. 1335-1339
ISSN
0002-337X
CODEN
NEOMB8

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
35010189
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
BORON ALLOYS; CHROMIUM ALLOYS; COBALT ALLOYS; CRYSTALLIZATION; ELECTRIC CONDUCTIVITY; IRON ALLOYS; METALLIC GLASSES; PHASE STUDIES; SILICON ALLOYS; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0400-1000 K
Descriptors DEC
ALLOYS; ELECTRICAL PROPERTIES; PHASE TRANSFORMATIONS; PHYSICAL PROPERTIES; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
11 refs., 3 figs.