Hardening effect in Ti-3Al-2.5V during high temperature deformation

High temperature deformation behavior of an alpha + beta titanium alloy Ti-3Al-2.5V has been investigated in the temperature range 830 deg. C to 910 deg. C by using the method of cross head speed cycling. On the basis of flow stress-strain rate and strain rate sensitivity data, it was found that the alloy exhibits a hardening effect in the entire temperature range studied, amount of hardening being significant at the highest test temperature of 910 deg. C which resulted in a degradation of superplastic properties of the alloy. Grain growth in beta-phase due to strain was considered responsible for the hardening effect observed