Performance of 9% chromium steel X 10 CrMoVNb 9 1 in short- and long-term tests. Pt. 2
- 1. Mannesmann Anlagenbau AG, Duesseldorf (Germany)
- 2. Technische Univ. Graz (Austria). Inst. fuer Werkstoffkunde, Festigkeitslehre und Materialpruefung
- 3. Mannesmann Forschungsinstitut, Duisburg (Germany)
Description
The steel X 10 CrMoVNb 9 1 demonstrates an excellent welding performance chiefly due to its relatively low carbon content. The hardness acceptance in the weld deposit is lower than in comparable materials and therefore the susceptibility to cracking following cooling from the operating temperature to room temperature is also lower. Preheating from 200 to 300deg C is sufficient to ensure cold crack-free welding. There is no susceptibility to cracking of the heat influence zone course grain structure with stress-free annealing. The heat influence zones of the welds demonstrate in all areas excellent toughness characteristics even after different types of heat treatment. (orig.)
Abstract (German)
Der Stahl X 10 CrMoVNb 9 1 weist vornehmlich wegen des relativ geringen C-Gehaltes ein gutes Schweissverhalten auf. Die Haerteannahme im Schweissgut ist geringer als bei vergleichbaren Werkstoffen und daher auch die Rissanfaelligkeit nach Abkuehlung von Arbeitstemperatur auf Raumtemperatur. Ein Vorwaermen auf 200 bis 300deg C reicht aus, um kaltrissfreie Schweissung sicherzustellen. Beim Spannungsarmgluehen ist eine Rissanfaelligkeit des WEZ-Grobkorngefueges nicht gegeben. Die Waermeeinflusszonen der Schweissnaehte zeigen in allen Bereichen auch nach verschiedenen Waermebehandlungen gute Zaehigkeitseigenschaften. (orig.)Additional details
Additional titles
- Subtitle (English)
- Welded joints
- Original title (German)
- Verhalten des 9%-Chromstahles X 10 CrMoVNb 9 1 im Kurz- und Langzeitversuch. T. 2
- Original subtitle (German)
- Schweissverbindungen.
Publishing Information
- Publisher
- Vulkan-Verl.
- Imprint Place
- Essen (Germany)
- ISBN
- 3-8027-2695-2
- Imprint Title
- Pipeline engineering. 5th edition
- Imprint Pagination
- 558 p.
- Journal Page Range
- p. 251-257.
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 23038627
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CREEP; FILLER METALS; HEAT AFFECTED ZONE; IMPACT STRENGTH; RUPTURES; STEEL-CR9MONBV; VICKERS HARDNESS; WELDABILITY; WELDED JOINTS
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CHROMIUM ALLOYS; CHROMIUM STEELS; FAILURES; FERRITIC STEELS; HIGH ALLOY STEELS; IRON ALLOYS; IRON BASE ALLOYS; JOINTS; MECHANICAL PROPERTIES; MOLYBDENUM ALLOYS; NIOBIUM ADDITIONS; STAINLESS STEELS; STEELS; VANADIUM ADDITIONS
Optional Information
- Notes
- Imprint:Rohrleitungstechnik. 5. Ausgabe.