Susceptibility of 17-4PH stainless steel to stress corrosion cracking in aqueous environments by electrochemical techniques

The susceptibility of a 17-4PH type steel to Stress Corrosion Cracking (SCC) in low pressure steam turbine environments was assessed using slow strain rate test at 90 Centigrade and at 1.35x10-6 seg-1. Environments tested included different concentrated solutions of NaCl, NaOH and Na2SO4. It was concluded that this steel is susceptible to SCC in 20 % NaCl and pH=3 and in 20 % NaCl pH=neutral but under cathodic polarisation. The electrochemical potential noise of the specimen was monitored during the test. The naturally fluctuations in potential were arise due to spontaneous brake protective film and were characteristics of the kind of corrosion like pit or stress corrosion cracking. After that using Fast Fourier Transformer (FFT) the noise data set were analyzed to obtain power spectral density plots which showed differences between general corrosion and localized corrosion. Polarization curves were carry out at two different rates and them showed the general behavior of the systems. (Author)