Thermal decomposition behavior of the co-precipitated carbonate precursor for La0.84Sr0.16MnO3

A carbonate precursor for lanthanum strontium manganite powder (La0.84Sr0.16MnO3 - LSM) was obtained by addition of an aqueous solution of nitrates of lanthanum, strontium and manganese into a bath of ammonium carbonate solution. The precipitate was filtered, washed, dried and dry ground for homogenization. The thermal decomposition behavior of the precursor was studied by simultaneous TG-DTA-EGA technique while the precursor and intermediates formed at different temperatures were characterized by FTIR and XRD techniques for decomposition of carbonate and compound formation. It exhibited a loss in weight and endotherms in stages in the temperature ranges of 20 to 260 deg C, 260 deg to 500 deg C, 500 deg to 600 deg C, 600 deg to 900 deg C. The loss of carbon dioxide was exhibited in the EGA data and FTIR spectra while phase formation was confirmed by XRD. A comparative study of all these results showed that the processes occurring at various temperature ranges (20 deg to 260 deg C, 260 deg to 500 deg C, 500 deg to 600 deg C, 600 deg to 900 deg C) are dehydration of adsorbed moisture and water of crystallization, decomposition of manganese hydroxycarbonate to manganese dioxide, lanthanum carbonate to lanthanum oxy-carbonate and interaction between lanthanum oxy-carbonate, manganese dioxide and strontium carbonate to form finally LSM. Even though decomposition of carbonates into oxides was complete at 900 deg C, phase pure compound formation occurred at 1100 deg C, under the conditions used. (author)