Behaviour of heat-resistant steels under multistage fatigue stress
Creators
Description
Four heat-resistant steels (10 CrMo 9 10, 28 CrMoNiV 4 9, X 22 CrMoV 12 1, X 6 CrNiMo 17 13), were used to examine the fatigue under multistage rectangular cyclic stress. The load cycles were made to be similar to the stress affecting power plant components. These are mainly cycles with decreasing and/or increasing stresses, with the temperature or both variables at the same time having been varied in some cases. As characteristical parameters of the modified life-fraction rule, the relative fracture life and for characterizing strains the relative strain life as well were determined. For the assessment of the relative life under any multistage stress, a new step hypothesis, applicable to all possible elementary stress steps, was developed. This hypothesis is able to predict even a consequential effect by means of additional rules. In comparison to this hypothesis, the simple life fraction rule which is unapt for single-stage stress, results in a somehow better prognosis of the fraction time and strain endurance limits under multistage stress. (orig./MM)
Abstract (German)
An vier warmfesten Staehlen (10 CrMo 9 10, 28 CrMoNiV 4 9, X 22 CrMoV 12 1, X 6 CrNiMo 17 13) wurde das Zeitstandverhalten unter mehrstufiger rechteckzyklischer Beanspruchung untersucht. Die Zyklen wurden in Anlehnung an die Beanspruchung von Kraftwerksbauteilen gestaltet. Vorwiegend handelt es sich um Zyklen mit fallender und/oder steigender Spannung, teilweise wurde auch die Temperatur oder beide Groessen gleichzeitig geaendert. Als Kennwerte der modifizierten Lebensdaueranteilregel wurden die relative Burchlebensdauer und fuer kennzeichnende Dehnungen auch die relative Dehnlebensdauer ermittelt. Zur Abschaetzung der relativen Lebensdauer unter beliebiger Mehrstufenbeanspruchung wurde eine neue, auf alle moeglichen elementaren Beanspruchungsschritte anwendbare Schritthypothese entwickelt, die ueber Zusatzregeln auch einen Folgeeinfluss erfassen kann. Gegenueber dieser Hypothese fuehrt die bei Einstufenbeanspruchung ungeeignete einfache Lebensdaueranteilregel bei Mehrstufenbeanspruchung zu einer noch etwas besseren Vorhersage der Bruchzeit und der Dehngrenzzeiten. (orig./MM)Additional details
Additional titles
- Original title (German)
- Verhalten warmfester Staehle unter mehrstufiger Zeitstandbeanspruchung
Publishing Information
- Imprint Title
- 16. lecture meeting of the Association for Heat-Resistant Steels and the Association for High-Temperature Materials, on 'Long-term performance of heat-resistant steels and high-temperature materials'. Thermal stress of materials. Proceedings
- Imprint Pagination
- 214 p.
- Journal Page Range
- p. 115-125.
Conference
- Title
- Long-time behavior of creep-resistant steels and high-temperature materials.
- Original Conference Title
- 16. Vortragsveranstaltung: Langzeitverhalten warmfester Staehle und Hochtemperaturwerkstoffe
- Acronym
- 16. lecture meeting
- Dates
- 26 Nov 1993.
- Place
- Duesseldorf (Germany).
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 26028312
- Subject category
- S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Conference, Non-conventional Literature
- Descriptors DEI
- CHROMIUM-MOLYBDENUM STEELS; CHROMIUM-NICKEL-MOLYBDENUM STEELS; CREEP; HYPOTHESIS; LIFETIME; MATHEMATICAL MODELS
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CHROMIUM ALLOYS; CHROMIUM STEELS; CHROMIUM-NICKEL STEELS; HIGH ALLOY STEELS; IRON ALLOYS; IRON BASE ALLOYS; MECHANICAL PROPERTIES; MOLYBDENUM ALLOYS; NICKEL ALLOYS; STAINLESS STEELS; STEELS; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- Imprint:16. Vortragsveranstaltung der Arbeitsgemeinschaft fuer warmfeste Staehle und Arbeitsgemeinschaft fuer Hochtemperaturwerkstoffe 'Langzeitverhalten warmfester Staehle und Hochtemperaturwerkstoffe'. Thermische Werkstoffbeanspruchung. Vortraege.