Mechanical properties and fracture mechanism of as-cast Mg77TM12Zn5Y6 (TM = Cu, Ni) bulk amorphous matrix composites

Comparative investigations on the microstructures, thermal stability and mechanical properties of Mg77Cu12Zn5Y6 and Mg77Ni12Zn5Y6 bulk metallic glass matrix composites were carried out by using scanning electron microscopy (SEM), DSC and compressive tester. The results show that the microstructure of as-cast samples with 3 mm in diameter for Cu-containing alloy is consisted of Mg flakes and dotted Mg2Cu phase in the amorphous matrix, while the as-cast Ni-containing alloy with the same diameter is mainly consisted of Mg flakes in the amorphous matrix. The glass transition temperature and supercooled liquid region are 413 K and 27 K for the Cu-containing, 443 K and 32 K for the Ni-containing amorphous matrix composites, respectively. The fracture strength, yield strength and plastic strain are 532 MPa, 390 MPa and 2.4% for the Cu-containing alloy, 667 MPa, 412 MPa and 7% for the Ni-containing alloy, respectively. Furthermore, the fracture mechanism for the amorphous matrix composites was discussed according to both the fracture surfaces and the stress-strain curves.