Structure and electronic properties of ordered binay thin-film compounds of rare earths with transition metals

The present thesis deals with preparation of structurally ordered thin-film compounds of the rare-earths Ce and Dy with the transition metals Pd, Rh, and Ni as well as with investigations of their crystalline and electronic structures. Typically 10 nm-thick films were grown in-situ by deposition of the rare-earth metals onto single crystalline transitionmetal substrates or alternatively by codeposition of both constituents onto a W(110) single crystal. In both cases deposition was followed by short-term annealing at temperatures of 400-1000 C to achieve crystalline order. The latter was analyzed by means of low-energy electron-diffraction (LEED) and evaluated on the basis of a simple kinematic theory. The electronic structure was investigated by means of angle-resolved photoemission (ARPES), partially exploiting synchrotron radiation from BESSY. The studies concentrate mainly on the behavior of the valence bands as a function of structure and composition of the thin films, particularly under consideration of surface phenomena. Measured energy dispersions were compared with results of LDA-LCAO calculations performed in the framework of this thesis. Observed shifts of the energy bands by up to 1 eV are attributed in the light of a simple model to incomplete screening of the photoemission final states. (orig.)