Hydrogen absorption by Pd-coated ZrNi prepared by using Barrel-Sputtering System

To improve the durability of hydrogen storage materials against surface poisoning by impurity gases, effectiveness of Pd-coating layer prepared by using a Barrel-Sputtering System was examined for ZrNi powder. The effectiveness of Pd-coating was evaluated by activation temperature, at which Pd/ZrNi poisoned by air could be activated to absorb hydrogen. Characterization of Pd-coated ZrNi (denoted as Pd/ZrNi) by scanning electron microscopy, electron probe microanalysis and X-ray diffraction showed that a uniform Pd-coating layer was formed with the barrel-sputtering system. It was found that the poisoned Pd/ZrNi sample could be activated even at 423 K to absorb hydrogen at room temperature. This exhibits remarkable contrast to bare ZrNi, which could be only activated appreciably above 1073 K. It is concluded that the Pd-coating by barrel sputtering is quite effective to avoid the effect of surface poisoning of powdery hydrogen storage materials. However, the activation at excessively high temperature resulted in the loss of high activity to absorb hydrogen. It was concluded that this phenomenon was associated with reactions between Pd and ZrNi to form PdZr and other byproducts