Evaluation of the electrochemical behavior of U2.5Zr7.5Nb and U3Zr9Nb uranium alloys in relation to the pH and the solution aeration

The Centro de Desenvolvimento da Tecnologia Nuclear (CDTN) is developing, in cooperation with the Centro Tecnologico da Marinha (CTMSP), the advanced nuclear plate type fuel for the second core of the land-based reactor prototype of the Laboratorio de Geracao Nucleo-Eletrica (LABGENE). Recent investigations have shown that the fuel made of uranium-based niobium and zirconium alloys reaches the best performance relative to other fuels, e.g. UO2. Niobium and Zirconium also increase the corrosion resistance and the mechanical strength of the uranium alloys. By means of electrochemical techniques the corrosion behavior of alloys U2.5Zr7.5Nb and U3Zr9Nb, developed at CDTN and heat treated in the temperature range of 200 deg C to 600 deg C, was assessed. The effect of the parameters pH and solution aeration was studied as well as the influence of zirconium and niobium alloying elements in the corrosion of uranium. The techniques used were open circuit potential, electrochemical impedance and potentiodynamic anodic polarization at room temperature. The tests were performed in a three-electrode electrochemical cell with Ag/AgCl (3M KCl) as the reference electrode and a platinum plate as the auxiliary electrode. The potentiodynamic polarization curves of uranium and its alloys in acidic solutions showed regions with anodic currents limited by a passive film. The presence of niobium and zirconium contributed for the formation of this film. The impedance data showed the presence of two semicircles in the Bode diagram, indicating the occurrence of two distinct electrochemical processes. The data were fitted to an equivalent circuit model in order to obtain parameters of the electrochemical processes and evaluate the effect of the studied variables. (author)