Experimental substantiation of the method of determining the critical temperature of brittleness in high-strength steels

Creators

  • 1. GNTs RF TsNIITMASH, Moscow (Russian Federation)

Description

A method to determine the critical temperature of brittleness for high-strength steels is stated. Studies of 38KhN3MFA steel samples used for the manufacture of fasteners for NPP equipment are carried out. It is shown that the temperature range of ductile-brittle transition of fastening steels is relatively wide and is 100-125 deg C. Impact strength dispersion of fastening steels in the transition region is a great deal less than the corresponding dispersion of vessel steels. The method is applicable to pearlitic steels and welded joints with a yield strength in the range of 687-1070 MPa

Abstract (Russian)

Изложена методика определения критической температуры хрупкости для сталей повышенной прочности. Исследования проведены на образцах из стали 38ХН3МФА, применяемой для изготовления крепежных деталей для оборудования АЭС. Показано, что интервал температур вязкохрупкого перехода сталей крепежного класса относительно широк и составляет 100-125 град С. Дисперсия ударной вязкости крепежных сталей в переходной области значительно меньше соответствующей дисперсии корпусных сталей. Методика применима к сталям перлитного класса и сварным соединениям с пределом текучести в диапазоне от 687 до 1070 МПа

Additional details

Additional titles

Original title (Russian)
Экспериментальное обоснование методики определения критической температуры хрупкости высокопрочных сталей

Publishing Information

Journal Title
Zavodskaya Laboratoriya
Journal Volume
66
Journal Issue
6
Journal Page Range
p. 45-48
ISSN
0321-4265
CODEN
ZVDLAU

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
33005321
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
DUCTILE-BRITTLE TRANSITIONS; FASTENERS; IMPACT STRENGTH; LOW ALLOY STEELS; NUCLEAR POWER PLANTS; TEMPERATURE RANGE 0273-0400 K; TENSILE PROPERTIES; TRANSITION TEMPERATURE; WELDED JOINTS
Descriptors DEC
ALLOYS; CARBON ADDITIONS; IRON ALLOYS; IRON BASE ALLOYS; JOINTS; MECHANICAL PROPERTIES; NUCLEAR FACILITIES; PHYSICAL PROPERTIES; POWER PLANTS; STEELS; TEMPERATURE RANGE; THERMAL POWER PLANTS; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
3 refs., 2 figs., 1 tab.