Reuse of scrap of Al and steel SAE 1045 in metal composite as alternative of recycling route powder metallurgy

Full text: The process of powder metallurgy in the production of parts through application of pressure on the selected ceramic or metal powders, which are subjected to a temperature of sintering for to occur consolidation of the components. The metal-mechanical industry is responsible for the generation of inputs from their manufacturing processes. This work aims to re-use of chips of Al and SAE 1045 steel by powder metallurgy of this is a viable and effective. This work is in the manufacture of a composite using Al 6060 metal matrix and steel 1045 as reinforcement (30%, 40%, 50%), under different compaction pressures (250MPa, 400MPa and 600MPa), analyzing the influence of compressibility in hardness of the compressed. The samples were sintered at a temperature of 500 ° C in an oven using resistive atmosphere of hydrogen for 45 minutes. After the procedures of the powder metallurgy technique were analyzed of the optical microscopy, x-ray diffraction, MEV and Rockwell hardness, which was found to be evaluated as not diffusibility between the steel and aluminum. (author)