Published 2018 | Version v1
Journal article Metadata-only

Mullite fabrication from natural kaolin and aluminium slag

Creators

Description

The structural transformations of kaolin–aluminium slag mixtures during heating were studied using differential thermal analysis (DTA), thermal gravimetric analysis (TGA), Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM). The amount of formed mullite increases with the firing temperature. At 1500°C, the mullitization of the mixture is almost complete. The morphology of the formed mullite is bimodal (primary and secondary phases). The primary mullite, formed from processing of kaolin by the gradual collapse of metakaolin from 990°C, has a shape of elongated crystals. The other hand, the secondary mullite formed by solution-precipitation from the glass phase in the presence of alumina particles has a shape of acicular grains.

Availability note (English)

Available doi: 10.1016/j.bsecv.2018.01.001

Abstract (Spanish)

Se estudiaron las transformaciones estructurales de las mezclas de caolín y escoria de aluminio durante el calentamiento mediante análisis térmico diferencial (ATD), análisis termogravimétrico (ATG), espectroscopía infrarroja por transformada de Fourier (EITF), análisis por difracción de rayos X (XRD, por sus siglas en inglés) y microscopia electrónica de barrido (MEB). La cantidad de mullita creada aumenta con la temperatura de cocción. A 1.500°C, la mullitización de la mezcla es casi completa. La morfología de la mullita creada es bimodal (fases primaria y secundaria). La mullita primaria, creada a partir del procesamiento del caolín por la paulatina desintegración del metacaolín a partir de 990°C, tiene una forma de cristales alargados. Además, la mullita secundaria creada por disolución-precipitación a partir de la fase de vidrio en presencia de partículas de alúmina tiene una forma de granos aciculares.

Additional details

Additional titles

Original title (Spanish)
Producción de mullita a partir de caolín natural y escoria de aluminio

Identifiers

DOI
10.1016/j.bsecv.2018.01.001;

Publishing Information

Journal Title
Boletin de la Sociedad Espanola de Ceramica y Vidrio
Journal Volume
57
Journal Issue
4
Journal Page Range
p. 169-177
ISSN
0366-3175
CODEN
BSCVB9

INIS

Country of Publication
Spain
Country of Input or Organization
Spain
INIS RN
49076394
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ALUMINIUM; DIFFERENTIAL THERMAL ANALYSIS; KAOLIN; MULLITE; PHASE TRANSFORMATIONS; SPECTROSCOPY
Descriptors DEC
CLAYS; ELEMENTS; INORGANIC ION EXCHANGERS; ION EXCHANGE MATERIALS; MATERIALS; METALS; MINERALS; OXIDE MINERALS; SILICATE MINERALS; THERMAL ANALYSIS