Electrochemical behaviour of brass in chloride solution concentrations found in eccrine fingerprint sweat

Highlights: • Corrosion of brass in NaCl concentrations found in eccrine sweat was investigated. • Concentrations < 0.2 M produce a layer of mainly zinc oxide after 24 h. • A concentration of 0.2 M enables active corrosion of brass at room temperature. • 0.2 M NaCl gives both zinc and copper dissolution. • 24-h immersion of brass in 0.2 M NaCl gives an oxide film thickness of 1.3 nm. - Abstract: In this work, the corrosion properties of α phase brass immersed in concentrations of aqueous NaCl solutions that are typically found in eccrine fingerprint sweat and range between 0.01 M and 0.2 M have been analysed. Analysis methods employed were electrochemical techniques, X-ray photoelectron spectroscopy and optical profiling. For NaCl concentrations <0.2 M, active corrosion did not occur although, after a period of 24 h, a passivating layer of mainly zinc oxide formed. At a concentration of 0.2 M active corrosion did occur, with measured corrosion potentials consistent with both brass and copper dissolution. A 1 h contact time at this concentration (0.2 M) resulted in the formation of a zinc oxide passivating layer with the surface ratio of zinc oxide to copper oxide increasing with time. Film thickness was calculated to be of the order of 1.3 nm after 24 h contact. Formation of oxide layers on brass by fingerprint sweat as observed here may well have implications for the successful investigation of crime by the visualisation of corrosion fingerprint ridge patterns or the reduction of hospital environmental contamination by hand contact with brass objects such as door handles or taps