Fundamental Study of Uranium Dendrites Electrochemically Separated in Molten Salt with the Presence of Cerium

In this study, uranium was electrochemically separated in the presence of cerium in eutectic LiCl-KCl at varying concentrations of cerium and varying overpotentials. Harvested dendrites were then examined and analyzed for their morphological features and elemental composition using various analytical techniques. Conclusions: Increasing the applied overpotential causes the dendrites to evolve from relatively simple and large platelet-like crystals (25 mV), to a grid-like network with crystals having jagged and smooth features (50 mV, 100 mV), and finally into a very chaotic and complex crystal morphology (200 mV) for all uranium-cerium compositions explored. Varying the uranium:cerium concentration ratio did not have much effect on the uranium dendrite morphologies. EDS results show that cerium is not co-deposited on the surface of the dendrite crystals, ICP-MS results do show a presence of cerium in the volumetric composition. This is likely due to salt occlusion during the dendrite formation. XRD has been performed on several samples at the 25 mV overpotential with 1 wt% U and 0 wt% Ce in the molten salt eutectic. These results indicate that there is not salt occlusion within the dendrites during electrochemical separation. Additionally, the uranium metal quickly oxidizes during preparation for XRD