Phase composition and hardening of steels from the systems Fe-Cr-Ni-Co-Mo with martensite-austenite structure

Creators

  • 1. MGTU im. N.Eh. Baumana, Moscow (Russian Federation)
  • 2. FGUP VIAM, Moscow (Russian Federation)

Description

Phase composition and mechanical properties of Fe-Cr-Ni-Co-Mo system maraging steels are studied depending on alloying, quenching and aging temperatures. Intermetallic phases are determined which harden martensite at various aging stages. The degree of hardening and changes of impact strength at cryogenic temperatures are compared for steels with different structures - martensitic and martensitic-austenitic ones at stages of maximum hardening and overaging. The effect of retained and transformed austenite on resistance to crack propagation under impact loading is determined for the steels in which martensite differs by its nature and by the quantity of strengthening phases

Abstract (Russian)

Изучены фазовый состав и механические свойства мартенситно-стареющих сталей системы Fe-Cr-Ni-Co-Mo в зависимости от легирования, температур закалки и старения. Определены интерметаллические фазы, упрочняющие мартенсит на различных стадиях старения. Проведено сравнение степени упрочнения и изменения ударной вязкости при криогенных температурах сталей с различными структурами - мартенситной и мартенситно-аустенитной на стадиях максимального упрочнения и перестаривания. Установлено влияние остаточного и ревертированного аустенита на сопротивление распространению трещин при ударном нагружении сталей, мартенсит которых различается по природе и количеству упрочняющих фаз

Additional details

Additional titles

Original title (Russian)
Фазовый состав и упрочнение сталей системы Фе-Cр-Ни-Cо-Мо с мартенситно-аустенитной структурой

Publishing Information

Journal Title
Metallovedenie i Termicheskaya Obrabotka Metallov
Journal Issue
no.4
Journal Page Range
p. 32-37
ISSN
0026-0819
CODEN
MTOMAX

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
39010694
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
AGE HARDENING; AUSTENITE; CHROMIUM-NICKEL-MOLYBDENUM STEELS; IMPACT STRENGTH; MARAGING STEELS; MARTENSITE; PHASE STUDIES; QUENCH AGING; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0400-1000 K; YIELD STRENGTH
Descriptors DEC
AGING; ALLOYS; CARBON ADDITIONS; CHROMIUM ALLOYS; CHROMIUM STEELS; CHROMIUM-MOLYBDENUM STEELS; CHROMIUM-NICKEL STEELS; HARDENING; HIGH ALLOY STEELS; IRON ALLOYS; IRON BASE ALLOYS; MARTENSITIC STEELS; MECHANICAL PROPERTIES; MOLYBDENUM ALLOYS; NICKEL ALLOYS; STAINLESS STEELS; STEELS; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
8 refs., 5 figs., 4 tabs.